Thermal stability of PA66 GF20 polyamide 66 is a mixture of 20% glass fiber reinforced polyamide 66, can be made into different colors, excellent high temperature resistant performance.
PA66 of 20% glass fiber and the thermal stability of modified level very mechanical parts, clutch bracket and;Electrical equipment, with high heat resistance and mechanical strength.
Physical properties of
Ash |
(20.0% 1 ISO3451/1) |
Conditioned |
600 ° C * 2 h |
Density |
(1 ISO1183 of 1280 kg/m3) |
Conditioned |
23 ° c. |
Shrinkage Parallel Flow |
(0.5-0.9% ISO294 1-4) |
Shrinkage Vertical Flow |
(0.8-1.1% I ISO294-4) |
Mechanical properties of
Tensile strength (142.0 MPa 1 ISO527) Conditioned |
5 mm/min |
The Tensile Strain at Break (2.5% I ISO527) Conditioned |
5 mm/min |
Notched Impact Strength (7.8 KJ/m2 IISO179) Conditioned |
1.0 J. |
Flexural Strength (234 mpa 1 iso178) Conditioned |
2 mm/min |
The Flexural Modulus (6869 MPa I ISO178) Conditioned |
2 mm/min |
Thermal performance
Melting Point |
(260 ° C I ISO11357) |
Hot Deformation Temperature |
(245 * C I ISO75) |
Conditioned |
1.8 MPa |
Flammability Class |
(ul94 HB 1) |
Conditioned |
mm |
Injection molding conditions
Drying Temperature |
130 ° c. |
Drying Time |
3 h. |
Cylinder Temperature |
280-300 ° C |
Nozzle Temperature |
* C. 280-300 |
Tooling Temperature |
* C. 80-100 |
Processing conditions for *;Only;For reference only, please according to actual condition to adjust